Advantage

Barrier Property

 
 
　 Gas Permeability at 25°C Moisture Vapor Transmission at 90%RH 37°C
(g·mil/100In2·d)**
（cm3(STP)·mil）(100in2/d·atm)*
H2 O2 CO2 N2 SO2 H2S Cl2
Parylene N 540 39 214 7.7 1890 795 74 1.5
Parylene C 110 7.2 7.7 1.0 11 13 0.35 0.21
Parylene D 240 32 13(a) 4.5 4.75 1.45 0.55 0.25
Parylene F _ _ _ _ _ _ _ _
Parylene HT _ 59.69 242.32 12.19 _ _ _ 0.56
Eposides（ER） 110 5-10 8 4 _ _ _ 1.79-2.38(a)
Silicones（SR） 45000 50000 300000 _ _ _ _ 4.4-7.9(a)
Urethanes(UR) _ 200 3000 80 _ _ _ 2.4-8.7(a)

(a）Iacari,J.J.and Brands,E.R.,Machine Design，May 25,1967，p.192
* ASTM   D 1434
* * ASTM  E  96



Parylene C Circuit Board Screening     
Insulation Resistance(ohms),MIL-STD-202.method 302 

parylene Thickness（um)
Initial
Measurement
 Precycle
Step 5
Cycle 3
Step 5
Cycle 7
Step 5
Cycle 10
Step 7
Cycle 10
23℃50%RH 23℃90%RH 65℃90%RH 65℃90%RH 65℃90%RH 25℃90%RH
50.8 2.0×1014 1.8×1013 2.3×1012 2.5×1011 1.4×1011 7.5×1012
38.1 5.0×1014 2.4×1013 8.6×1011 1.9×1011 1.1×1011 5.2×1012
25.4 2.0×1014 9.2×1012 8.1×1011 3.4×1011 1.3×1011 6.3×1012
12.7 5.0×1014 2.3×1013 4.1×1012 2.4×1011 1.1×1011 4.7×1012
7.6 5.0×1014 2.7×1013 4.4×1012 9.0×1010 4.7×1010 2.9×1012
2.5 5.0×1014 3.2×1010 1.3×1011 1.1×1011 6.4×1010 2.3×1012